ACIS (BSI CCD) Line(s) for Si Target & Si Filters ---------------------------------------------------------------------- Target composition: Si Filter composition: Si at density 2.329 g/cm^3 t_filter = { 0, 1, 2, 4, 6, 8, 10 } / mu_linear( E_filter ) E-filter (keV) 1.739 t_filter (micron) 0 12.2 24.5 48.9 73.4 97.8 122. ---------------------------------------------------------------------- Si@3.680 kV; sin(ta) = 0.50 t_filter (micron) 0 12.2 24.5 48.9 73.4 97.8 122. (keV) 0.547 1.34 1.51 1.64 1.69 1.72 1.73 sigma_E (keV) 0.745 0.713 0.581 0.403 0.285 0.203 0.145 Total (c/s/mA) 46900. 5080. 1610. 197. 25.8 3.47 0.472 0.0915 (c/s/mA) 5.71 0 0 0 0 0 0 0.0925 (c/s/mA) 2.73 0 0 0 0 0 0 1.739 (c/s/mA) 9640. 3550. 1300. 177. 23.9 3.23 0.437 1.836 (c/s/mA) 159. 67.5 28.7 5.19 0.937 0.169 0.03 0.0915 (line frac) 0 0 0 0 0 0 0 0.0925 (line frac) 0 0 0 0 0 0 0 1.739 (line frac) 0.205 0.698 0.811 0.897 0.927 0.932 0.926 1.836 (line frac) 0.003 0.013 0.017 0.026 0.036 0.048 0.064 ---------------------------------------------------------------------- Si@5.520 kV; sin(ta) = 0.50 t_filter (micron) 0 12.2 24.5 48.9 73.4 97.8 122. (keV) 0.777 1.45 1.57 1.66 1.7 1.71 1.7 sigma_E (keV) 0.851 0.687 0.566 0.445 0.418 0.461 0.566 Total (c/s/mA) 98900. 15900. 5250. 664. 88.8 12.2 1.71 0.0915 (c/s/mA) 7.75 0 0 0 0 0 0 0.0925 (c/s/mA) 3.72 0 0 0 0 0 0 1.739 (c/s/mA) 32700. 12000. 4430. 599. 81.1 11. 1.48 1.836 (c/s/mA) 540. 229. 97.5 17.6 3.19 0.576 0.104 0.0915 (line frac) 0 0 0 0 0 0 0 0.0925 (line frac) 0 0 0 0 0 0 0 1.739 (line frac) 0.33 0.758 0.843 0.902 0.913 0.901 0.869 1.836 (line frac) 0.005 0.014 0.018 0.026 0.035 0.047 0.06 ---------------------------------------------------------------------- Si@7.360 kV; sin(ta) = 0.50 t_filter (micron) 0 12.2 24.5 48.9 73.4 97.8 122. (keV) 0.919 1.48 1.58 1.65 1.65 1.61 1.57 sigma_E (keV) 0.899 0.742 0.693 0.802 1.13 1.63 2.13 Total (c/s/mA) 157000. 30600. 10400. 1400. 212. 38.7 9.52 0.0915 (c/s/mA) 8.27 0 0 0 0 0 0 0.0925 (c/s/mA) 3.98 0 0 0 0 0 0 1.739 (c/s/mA) 63700. 23400. 8620. 1170. 158. 21.4 2.89 1.836 (c/s/mA) 1050. 448. 191. 34.4 6.23 1.12 0.203 0.0915 (line frac) 0 0 0 0 0 0 0 0.0925 (line frac) 0 0 0 0 0 0 0 1.739 (line frac) 0.406 0.765 0.827 0.834 0.746 0.552 0.303 1.836 (line frac) 0.006 0.014 0.018 0.024 0.029 0.029 0.021 ---------------------------------------------------------------------- Si@9.200 kV; sin(ta) = 0.50 t_filter (micron) 0 12.2 24.5 48.9 73.4 97.8 122. (keV) 1.02 1.5 1.59 1.64 1.64 1.63 1.65 sigma_E (keV) 0.923 0.794 0.807 1.1 1.65 2.27 2.69 Total (c/s/mA) 217000. 48100. 16700. 2390. 424. 107. 39.7 0.0915 (c/s/mA) 7.9 0 0 0 0 0 0 0.0925 (c/s/mA) 3.82 0 0 0 0 0 0 1.739 (c/s/mA) 100000. 36900. 13600. 1840. 248. 33.6 4.55 1.836 (c/s/mA) 1660. 707. 301. 54.3 9.82 1.78 0.32 0.0915 (line frac) 0 0 0 0 0 0 0 0.0925 (line frac) 0 0 0 0 0 0 0 1.739 (line frac) 0.46 0.767 0.81 0.767 0.585 0.314 0.114 1.836 (line frac) 0.007 0.014 0.017 0.022 0.023 0.016 0.008 ----------------------------------------------------------------------