HRC-I (CsI Coated MCP) Line(s) for Si Target & Si Filters ---------------------------------------------------------------------- Target composition: Si Filter composition: Si at density 2.329 g/cm^3 t_filter = { 0, 1, 2, 4, 6, 8, 10 } / mu_linear( E_filter ) E-filter (keV) 1.739 t_filter (micron) 0 12.2 24.5 48.9 73.4 97.8 122. ---------------------------------------------------------------------- Si@3.680 kV; sin(ta) = 0.50 t_filter (micron) 0 12.2 24.5 48.9 73.4 97.8 122. (keV) 0.542 1.32 1.49 1.63 1.69 1.72 1.73 sigma_E (keV) 0.741 0.727 0.598 0.419 0.297 0.212 0.152 Total (c/s/mA) 18700. 2050. 641. 77.7 10.2 1.36 0.185 0.0915 (c/s/mA) 270. 0 0 0 0 0 0 0.0925 (c/s/mA) 135. 0 0 0 0 0 0 1.739 (c/s/mA) 3790. 1390. 512. 69.3 9.38 1.27 0.171 1.836 (c/s/mA) 61.5 26.1 11.1 2.01 0.363 0.065 0.011 0.0915 (line frac) 0.014 0 0 0 0 0 0 0.0925 (line frac) 0.007 0 0 0 0 0 0 1.739 (line frac) 0.202 0.679 0.799 0.892 0.924 0.931 0.926 1.836 (line frac) 0.003 0.012 0.017 0.025 0.035 0.048 0.063 ---------------------------------------------------------------------- Si@5.520 kV; sin(ta) = 0.50 t_filter (micron) 0 12.2 24.5 48.9 73.4 97.8 122. (keV) 0.769 1.43 1.56 1.66 1.7 1.71 1.72 sigma_E (keV) 0.834 0.673 0.546 0.406 0.354 0.374 0.459 Total (c/s/mA) 38800. 6250. 2060. 259. 34.5 4.7 0.653 0.0915 (c/s/mA) 366. 0 0 0 0 0 0 0.0925 (c/s/mA) 184. 0 0 0 0 0 0 1.739 (c/s/mA) 12800. 4730. 1740. 235. 31.8 4.31 0.583 1.836 (c/s/mA) 209. 88.9 37.8 6.83 1.23 0.223 0.04 0.0915 (line frac) 0.009 0 0 0 0 0 0 0.0925 (line frac) 0.004 0 0 0 0 0 0 1.739 (line frac) 0.331 0.755 0.845 0.908 0.923 0.916 0.892 1.836 (line frac) 0.005 0.014 0.018 0.026 0.035 0.047 0.061 ---------------------------------------------------------------------- Si@7.360 kV; sin(ta) = 0.50 t_filter (micron) 0 12.2 24.5 48.9 73.4 97.8 122. (keV) 0.906 1.48 1.58 1.66 1.67 1.64 1.59 sigma_E (keV) 0.869 0.694 0.626 0.7 1.01 1.5 2.04 Total (c/s/mA) 61300. 11900. 4020. 531. 78.2 13.6 3.14 0.0915 (c/s/mA) 391. 0 0 0 0 0 0 0.0925 (c/s/mA) 196. 0 0 0 0 0 0 1.739 (c/s/mA) 25000. 9210. 3390. 458. 62. 8.39 1.14 1.836 (c/s/mA) 408. 174. 73.8 13.3 2.41 0.435 0.078 0.0915 (line frac) 0.006 0 0 0 0 0 0 0.0925 (line frac) 0.003 0 0 0 0 0 0 1.739 (line frac) 0.408 0.775 0.843 0.862 0.793 0.617 0.361 1.836 (line frac) 0.006 0.014 0.018 0.025 0.03 0.032 0.025 ---------------------------------------------------------------------- Si@9.200 kV; sin(ta) = 0.50 t_filter (micron) 0 12.2 24.5 48.9 73.4 97.8 122. (keV) 1. 1.5 1.6 1.66 1.66 1.65 1.66 sigma_E (keV) 0.885 0.728 0.719 0.975 1.52 2.19 2.66 Total (c/s/mA) 84700. 18500. 6380. 891. 151. 35.7 12.7 0.0915 (c/s/mA) 373. 0 0 0 0 0 0 0.0925 (c/s/mA) 188. 0 0 0 0 0 0 1.739 (c/s/mA) 39400. 14500. 5330. 721. 97.5 13.2 1.79 1.836 (c/s/mA) 644. 274. 116. 21. 3.8 0.687 0.124 0.0915 (line frac) 0.004 0 0 0 0 0 0 0.0925 (line frac) 0.002 0 0 0 0 0 0 1.739 (line frac) 0.464 0.783 0.834 0.808 0.646 0.369 0.14 1.836 (line frac) 0.007 0.014 0.018 0.023 0.025 0.019 0.009 ----------------------------------------------------------------------